Forged Fittings
Forged Fittings
Forged fittings are made of A105 (carbon steel), stainless steel or nickel alloy. These fittings are thicker, heavier and are intended for heavy industrial use. Forged fittings are used for piping systems below 2 or 4 inches in diameter.
Forged fitting are the finished products and are created by forging. They are passed through heat and cold temperatures and then formed by pressing or hammering and then shaped into various forms.
RANGE : 45° and 90° Elbows, Concentric and Eccentric Reducers, Equal and Reducing Tees, 180° Return Bends and Caps
Size : –½” to 80” NB.
FORM :: SEAMLESS & WELDED LONG RADIUS & SHORT RADIUS ELBOW 90 DEG, LONG RADIUS ELBOW 45 DEG, Long Radius & Short Radius Elbow 90 Deg, Long Radius Elbow 45 Deg, Long Radius & Short Radius Elbow 180 Deg ( Return Bend ) , Reducing Elbow, Equal Tee, Un Equal Tee, Crosses, Concentric Reducer, Eccentric Reducer, Long Stubend, Short Stubend, Coller, Pipe Cap, Long Radius Bends R =3 D, 5 D, 6 D, 8 D,10 D & 20 D In 15 Deg,30 Deg, 60 Deg & 90 Deg And Drawing Bassed Butt Weld Fitting Customised .
Packing: – Superior Quality Polythene Bag and Standard Wooden Box.
| Stainless & Duplex Steel | |
|---|---|
| Stainless Steel | ASTM / ASME SA 403 GR WP “S” / “W” / ” WX” 304 , 304L , 304H, 304N , 304LN , 309, 310H , 316 , 316H , 317 , 317L , 321 , 321H , 347 , 347 H |
| Duplex Steel | ASTM / ASME SA 815 UNS NO.S 31803 , S 32205 , S 32550 , S 32750 , S 32760 . |
| Nickel & Copper Alloy | |
|---|---|
| Nickel Alloy | ASTM / ASME SB 336 UNS 2200 ( NICKEL 200 ) , UNS 2201 (NICKEL 201 ) , UNS 4400 (MONEL 400 ), UNS 8020 ( ALLOY 20 / 20 CB 3 ) , UNS 8825 INCONEL (825) , UNS 6600 (INCONEL 600 ) , UNS 6601 ( INCONEL 601 ) , UNS 6625 (INCONEL 625) , UNS 10276 ( HASTELLOY C 276 ) |
| Copper Alloy |
ASTM / ASME SB 111 UNS NO.C 10100 , C 10200 , C 10300 , C 10800 , C 12000, C 12200, C 70600 , C 71500 . ASTM / ASME SB 466 UNS NO.C 70600 ( CU -NI- 90/10) , C 71500 ( CU -NI- 70/30) |
| Carbon & Alloy Steel | |
|---|---|
| Carbon Steel |
ASTM / ASME A 234 WPB , WPC ASTM / ASME A 860 WPHY 42 , WPHY 46 , WPHY 52 , WPH 60 , WPHY 65 & WPHY 70 . |
| Alloy Steel | ASTM / ASME A 234 WP 1, WP 5, WP 9, WP 11, WP 12, WP 22, WP 23, WP 91 |
Chemical Composition
| Element | SS 304 | SS 304L | 304H | SS 309 | SS 310 | SS 310S | SS 316 | SS 316L | SS 317 | SS 317L | SS 321 | SS 321 H | SS 347 | SS 347H | SS 904L |
| Ni | 8.0 – 11.0 | 8.0 – 13.0 | 0.03 max |
12-15 | min: 8.0 max: 12.0 | 19-22 | min: 10.0 max: 14.0 |
min: 10.0 max: 14.0 |
11 – 14 | 11 – 15 | max:0.10 | max:0.10 | min: 9.0 max: 13.0 |
min: 9.0 max: 13.0 |
0.045 |
| C | 0.08 | 0.35 | min: 18.0 max:20.0 |
max : 0.2 | max : 0.25 | max : 0.08 | max : 0.08 | max :0.03 | max : 0.08 | max : 0.035 | max:0.08 | min:0.04 max:0.10 |
max : 0.08 | min: 0.04 max: 0.10 |
0.02 |
| Mn | max : 2.0 | max : 2.0 | min: 8.0 max: 10.5 |
max : 2.0 | max : 2.0 | max :2.00 | max : 2.0 | max : 2.0 | max : 2 | max : 2 | max:2.0 | max:2.0 | max : 2.0 | max : 2.0 | 4.0-5.0 |
| P | max : 0.045 | max : 0.045 | max : 0.75 | max : 0.045 | max : 0.045 | 0.045 | max : 0.045 | max : 0.045 | max : 0.040 | max : 0.040 | Max : 0.045 | Max : 0.045 | max : 0.04 | max : 0.03 | 0.035 |
| S | max : 0.03 | max : 0.03 | max : 2.0 | max : 0.03 | max : 0.03 | 0.03 | max : 0.03 | max : 0.03 | max : 0.03 | max : 0.03 | max : 0.03 | max : 0.045 | max : 0.30 | max : 0.30 | 1.0 |
| Si | max : 1.0 | max : 1.0 | min: 0.04 max:0.10 |
max : 1.0 | max : 1.50 | max : 1.50 | max : 0.75 | max : 0.75 | max : 1 | max : 1 | max : 0.75 | min: 18.0 max:20.0 |
max : 0.75 | max : 0.75 | – |
| Cr | 18.0 – 20.0 | 18.0 – 20.0 | max : 0.045 | 22 – 24 | 24-26 | 24-26 | min: 16.0 max: 18.0 |
min: 16.0 max: 18.0 |
18 – 20 | 18 – 20 | min:17.0 max:19.0 |
min:17.0 max:19.0 |
min : 17.0 max : 20.0 | min : 17.0 max : 20.0 | 19.0-23.0 |
Mechanical Properties
| Element | SS 304 | SS 304L | SS 304 H | SS 309 | SS 310 | SS 310S | SS 316 | SS 316L | SS 317 | SS317 L | SS 321 | SS 321L | SS 347 | SS 347H | SS 904L |
| Density | 8.0 g/cm3 | 8.0 g/cm3 | at 68 °F 0.285 |
at 68 °F 0.285 |
at 68 °F 0.285 |
at 68 °F 0.285 |
at 68°F 0.290 | at 68°F 0.290 | 8.0 g/cm3 | 8.0 g/cm3 | a at 68
°F 0.286t |
at 68 °F 0.286 |
at 68 °F 0.286 |
at 68 °F 0.286 |
7900 |
| Melting Point | 1400 °C (2550 °F) | 1400 °C (2550 °F) | 1454 °C (2650 °F) | 1454 °C (2650 °F) | |||||||||||
| Tensile Strength | Psi – 75000 , MPa – 515 | Psi – 75000 , MPa – 515 | 75 | 40 | Psi – 75000 , MPa – 515 | Psi – 75000 , MPa – 515 | 75 | 70 | Psi – 75000 , MPa – 515 | Psi – 75000 , MPa – 515 | 75 | 75 | 75 | 75 | 490 |
| Yield Strength (0.2%Offset) | Psi – 30000 , MPa – 205 | Psi – 30000 , MPa – 205 | 3030 30 | 30 | Psi – 30000 , MPa – 205 | Psi – 30000 , MPa – 205 | 30 | 25 | Psi – 30000 , MPa – 205 | Psi – 30000 , MPa – 205 | 30 | 30 | 30 | 30 | 220 |
| Elongation | 35 | 35 | 40 | 40 | 40 | 40 | 40 | 40 | 35 | 35 | 40 | 40 | 40 | 40 | 36 |